GLAÇURES
à CÔNE 6 en
RÉDUCTION
par
Diana PANCIOLI
RECETTE
N°3
|
-
-
|
FICHE N°
3
|
|
Nom de la Recette
: JAUNE FRAIS
|
|
Cône :
6
|
Aspect : SEMI
BRILLANT
|
Couleur :
JAUNE
|
|
Cuisson :
REDUCTION
|
|
|
|
|
|
|
Seger
|
%
poids
|
%
Molaire
|
|
Li2O
|
-
|
-
|
-
|
|
Na2O
|
0.166
|
4.47
|
5.06
|
|
K2O
|
0.053
|
2.19
|
1.63
|
|
MgO
|
0.219
|
3.83
|
6.66
|
|
CaO
|
0.294
|
17.85
|
8.15
|
|
SrO
|
-
|
-
|
-
|
|
BaO
|
0.267
|
17.85
|
8.15
|
|
ZnO
|
-
|
-
|
-
|
|
PbO
|
-
|
-
|
-
|
|
|
|
|
|
|
S/total
Alcalins
|
0.220
|
6.66
|
6.69
|
|
total des
fondants
|
1.000
|
35.52
|
30.49
|
|
Al2O3
|
0.263
|
11.65
|
8.01
|
|
B2O3
|
0.010
|
0.30
|
0.30
|
|
Fe2O3
|
0.002
|
0.16
|
0.07
|
|
SiO2
|
2.004
|
52.31
|
61.09
|
|
TiO2
|
0.001
|
0.03
|
0.02
|
|
P2O5
|
0.000
|
0.01
|
0.01
|
|
SiO2/Al2O3
|
7.62
|
|
Coef.
Dilat.
|
85.18
|
|
Perte au
feu
|
12.99
|
|
Coût
en $ par livre de glaçure
:
|
0.98
|
|
Photo de la
glaçure
|
- Commentaires :
-
- Dérivée du
« jaune d'Alfred » à cône 10
Cette glaçure d’un jaune froid tourne au
bleu-clair lorsqu’appliquée de
façon épaisse et à un brun chaud
là où elle est mince.Le strontium ne
fonctionne pas comme produit de remplacement pour le
baryum dans cette glaçure. La couleur jaune est
complètement perdue avec le strontium. Ce n'est
pas une glaçure pour le revêtement
intérieur des outils alimentaires.
- Elle lixivie(relâche)
le baryum à 7.25 mg/l.
- Une application d’une
épaisseur moyenne est
suggérée.
-
-
-
MATIÈRES
NORD-AMÉRICAINES UTILISÉES
DANS CES RECETTES :
-
- FRITTES :
- Ferro 3110
: K2O 0,064 Na2O 0,644 CaO 0,293 Al2O3 0,095 B2O3
0,097 SiO2 3,003
- Fritte
Ferro 3134 : Na2O 0,317 CaO 0,683 B2O3 0,634 SiO2
1,476
- Fritte
Ferro 3195 : Na2O 0,313 CaO 0,686 Al2O3 0,404 B2O3
1,099 SiO2 2,751
-
-
- Matières
premières et équivalents
Européens :
-
- Kentuky
OM#4 ball clay (Old Mine #4): OM #4 is a
fine-grained ball clay with good plasticity and
strength. It is very common in glaze recipes. It
undergoes a sudden color shift around cone 8-9, from
straw yellow to solid gray [IMC]. Composition
% 0.3 Na2O 1.0 K2O 0.4 MgO 0.3 CaO 27.9 Al2O3 55.2
SiO2 1.2 TiO2 1.1 Fe2O3 12.6 Perte au feu.
-
- Kona
F4 Feldspar : Commonly used soda feldspar;
used in porcelains because of its low iron content.
Composition % 6.90 Na2O 4.8 K2O 0.05 MgO 1.70 CaO
19.60 Al2O3 66.80 SiO2 0.04 Fe2O3 0.20 Perte au feu =
Feldspath CR-79 (DAM - IMERYS)
-
- Custer
Feldspar : Commonly used potash feldspar. Can
be used to substitute for Keystone,
BuckinghamFeldspath CR-79 (DAM) , Yankee, or Kingman
feldspars. Composition % 2.91 Na2O 10.28 K2O 0.30 CaO
17.35 Al2O3 69.00 SiO2 0.12 Fe2O3 0.04 Perte au feu =
Feldspath ICE 10B (DAM - IMERYS)
-
- Epsom
salts : magnesium sulfate. Highly soluble;
used in small quantities (0.1%-1%) as a flocculant in
slips and glazes. Many sources recommend making a
concentrated solution, then adding the solution to the
mixed glaze. Composition Molaire : MgO SO3 7 H2O.
-
- Argile
Red Art : An iron-rich clay consisting of
clay/shale deposits from a prehistoric lake bed.
Contains 40% illite, 10% kaolinite, 7% iron oxide, and
15% mixed layered clays. Composition % 0.38 Na2O 4.15
K2O 1.59 MgO 0.26 CaO 15.51 Al2O3 64.95 SiO2 1.09 TiO2
7.05 Fe2O3 0.22 P2O5 4.80 Perte au feu.
-
- Cornwall
stone : Composition % 3.30 Na2O 4.31 K2O 0.14
MgO 1.81 CaO 16.31 Al2O3 73.80 SiO2 0.15 TiO2 0.20
Fe2O3
-
- Spodumène
Foote : Composition % Li2O 7.26 SiO2 63.84
Al2O3 28.61 Fe2O3 0.19 CaO 0.04 MgO trace Perte au feu
0.16
-
- EPK
Kaolin (Edgar Plastic Kaolin, origine Floride) :
CaO 0.18 MgO 0.10 K2O 0.33 Na2O 0.06 P2O5 0.24
TiO2 0.37 Al2O3 37.36 SiO2 45.73 Fe2O3 0.79 Perte au
feu 13.20
-
-
-
- Smart2000.fr
©
Avril 2009
-
FRANCE
- Contact
: Smart2000@wanadoo.fr
- Document
pour CONSULTATION PRIVÉE uniquement - Toute
reproduction totale ou partielle est
interdite
-
-
-
-
- Smart2000.fr
le site
dédié aux passionnés de
céramique
-
- Smart2000
- FRANCE sur https://smart2000.fr/
-
- This
entire page Copyright © 2009-2023, All Rights
Reserved.
- Les
textes et les photos restent la
propriété de leur auteurs, ils ne
peuvent être réutilisés sans un
accord préalable. Nous
consulter.
|