- Sommaire
-
-
-
|
GLAÇURES
à CÔNE 6 en
RÉDUCTION
par
Diana PANCIOLI
RECETTE
N°21
|
-
-
|
FICHE N°
21
|
|
Nom de la Recette
: CENDRE BRUNE
|
|
Cône :
6
|
Aspect :
MAT
|
Couleur :
BRUN MOYEN
|
|
Cuisson :
REDUCTION
|
|
|
|
|
Seger
|
%
poids
|
%
Molaire
|
|
Li2O
|
-
|
-
|
-
|
|
Na2O
|
0.004
|
0.09
|
0.11
|
|
K2O
|
0.077
|
2.51
|
1.86
|
|
MgO
|
0.072
|
1.01
|
1.76
|
|
CaO
|
0.658
|
12.83
|
15.97
|
|
SrO
|
-
|
-
|
-
|
|
BaO
|
0.188
|
10.04
|
4.57
|
|
ZnO
|
-
|
-
|
-
|
|
PbO
|
-
|
-
|
-
|
|
|
|
|
|
|
S/total
Alcalins
|
0.081
|
2.60
|
1.97
|
|
total des
fondants
|
1.000
|
26.48
|
24.26
|
|
Al2O3
|
0.365
|
12.92
|
8.85
|
|
B2O3
|
-
|
-
|
-
|
|
Fe2O3
|
0.077
|
4.29
|
1.88
|
|
SiO2
|
2.653
|
55.34
|
64.34
|
|
TiO2
|
0.028
|
0.76
|
0.67
|
|
P2O5
|
-
|
-
|
-
|
|
SiO2/Al2O3
|
7.27
|
|
Coef.
Dilat.
|
74.83
|
|
Perte au
feu
|
14.90
|
|
Coût
en $ par livre de glaçure
:
|
0.41
|
|
Photo de la
glaçure
|
Commentaires :
- Dérivé du
«Brun Jaune Cassé» d'Emmanuel Cooper.
- La substitution du strontium
dans cette glaçure était moins que
réussie. La glaçure originale a une
complexité extérieure qui a
été perdue avec la substitution. Ce
n'est pas une glaçure pour le revêtement
des objets alimentaires.
- Une application de mince
à moyenne est suggérée.
- Les tests de lixiviation
(relâchement) ne sont pas encore
sortis.
-
-
-
MATIÈRES
NORD-AMÉRICAINES UTILISÉES
DANS CES RECETTES :
-
- FRITTES :
- Ferro 3110
: K2O 0,064 Na2O 0,644 CaO 0,293 Al2O3 0,095 B2O3
0,097 SiO2 3,003
- Fritte
Ferro 3134 : Na2O 0,317 CaO 0,683 B2O3 0,634 SiO2
1,476
- Fritte
Ferro 3195 : Na2O 0,313 CaO 0,686 Al2O3 0,404 B2O3
1,099 SiO2 2,751
-
-
- Matières
premières et équivalents
Européens :
-
- Kentuky
OM#4 ball clay (Old Mine #4): OM #4 is a
fine-grained ball clay with good plasticity and
strength. It is very common in glaze recipes. It
undergoes a sudden color shift around cone 8-9, from
straw yellow to solid gray [IMC]. Composition
% 0.3 Na2O 1.0 K2O 0.4 MgO 0.3 CaO 27.9 Al2O3 55.2
SiO2 1.2 TiO2 1.1 Fe2O3 12.6 Perte au feu.
-
- Kona
F4 Feldspar : Commonly used soda feldspar;
used in porcelains because of its low iron content.
Composition % 6.90 Na2O 4.8 K2O 0.05 MgO 1.70 CaO
19.60 Al2O3 66.80 SiO2 0.04 Fe2O3 0.20 Perte au feu =
Feldspath CR-79 (DAM - IMERYS)
-
- Custer
Feldspar : Commonly used potash feldspar. Can
be used to substitute for Keystone,
BuckinghamFeldspath CR-79 (DAM) , Yankee, or Kingman
feldspars. Composition % 2.91 Na2O 10.28 K2O 0.30 CaO
17.35 Al2O3 69.00 SiO2 0.12 Fe2O3 0.04 Perte au feu =
Feldspath ICE 10B (DAM - IMERYS)
-
- Epsom
salts : magnesium sulfate. Highly soluble;
used in small quantities (0.1%-1%) as a flocculant in
slips and glazes. Many sources recommend making a
concentrated solution, then adding the solution to the
mixed glaze. Composition Molaire : MgO SO3 7 H2O.
-
- Argile
Red Art : An iron-rich clay consisting of
clay/shale deposits from a prehistoric lake bed.
Contains 40% illite, 10% kaolinite, 7% iron oxide, and
15% mixed layered clays. Composition % 0.38 Na2O 4.15
K2O 1.59 MgO 0.26 CaO 15.51 Al2O3 64.95 SiO2 1.09 TiO2
7.05 Fe2O3 0.22 P2O5 4.80 Perte au feu.
-
- Cornwall
stone : Composition % 3.30 Na2O 4.31 K2O 0.14
MgO 1.81 CaO 16.31 Al2O3 73.80 SiO2 0.15 TiO2 0.20
Fe2O3
-
- Spodumène
Foote : Composition % Li2O 7.26 SiO2 63.84
Al2O3 28.61 Fe2O3 0.19 CaO 0.04 MgO trace Perte au feu
0.16
-
- EPK
Kaolin (Edgar Plastic Kaolin, origine Floride) :
CaO 0.18 MgO 0.10 K2O 0.33 Na2O 0.06 P2O5 0.24
TiO2 0.37 Al2O3 37.36 SiO2 45.73 Fe2O3 0.79 Perte au
feu 13.20
-
-
-
- Smart2000.fr
©
Avril 2009
-
FRANCE
- Contact
: Smart2000@wanadoo.fr
- Document
pour CONSULTATION PRIVÉE uniquement - Toute
reproduction totale ou partielle est
interdite
-
-
-
-
- Smart2000.fr
le site
dédié aux passionnés de
céramique
-
- Smart2000
- FRANCE sur https://smart2000.fr/
-
- This
entire page Copyright © 2009-2023, All Rights
Reserved.
- Les
textes et les photos restent la
propriété de leur auteurs, ils ne
peuvent être réutilisés sans un
accord préalable. Nous
consulter.
|